Understanding Polymer Clay Glaze, Sealer, and Varnish

No matter what type of things you like to make with polymer clay, sooner or later, the question of sealers comes up. It’s common for new polymer clay crafters to have misconceptions about the subject of varnishes, sealers, and clear coatings. Confused readers often ask me about the differences between types of coatings, particularly how and when you’d want to use them. In this article, I’ll try to clear up confusion and help with understanding polymer clay glazes, sealers, and varnishes.

Note: I recently tested 41 different glazes, sealers, and varnishes on five different brands of clay. You can see which of them scored well and which got sticky or peeled off. I found that each product behaved differently on each brand of clay. Varnishes and dimensional glazes have high failure rates when used on polymer clay. 

Sealers are Not Necessary

Polymer clay, when cured, is vinyl – similar to a kiddie pool, tablecloth on your deck table, or beach ball. We would never think of varnishing or sealing a beach ball to protect it, right? Likewise, there’s no need to seal polymer clay. Adding a clear coating, glaze, or varnish will not make a polymer clay project more durable, waterproof, weatherproof, or heatproof. It will not make a project stronger or protect against breakage. If anything, adding a coating to polymer clay increases the likelihood of it being ruined. Most polymer clay glazes, sealers, varnishes, or clear coatings can become sticky, peel easily, turn cloudy, or crack. This will depend on the brands involved and the conditions they’re exposed to.

You only need to seal and protect what you put ON the surface of your polymer clay project. When you apply mica powders, chalks, glitter, or metal leaf to the surface of your polymer clay project, it will need to be protected if the item is subject to wear. Note that light dustings of chalk or mica, such as rosy cheeks on a sculpture, do not need to be sealed. The same holds true for dots of paint and antiquing in the recessed areas of a design.

Polymer clay is not glossy after baking. You can sand, buff, and polish the clay itself (see below), or you can apply a glossy varnish. To make your clay project less shiny, you could apply a matte varnish. Note that adding a glossy varnish can make translucent polymer clay seem more clear. Just like wetting a beach pebble, a glaze or varnish can make clay appear brighter and/or more translucent.



This includes artists’ varnishes, wood varnishes, glazes sold by the clay manufacturers themselves, and even floor finishes. These products are typically clear to milky white liquids. Some are off-white. Once dried, most will form a stretchy plastic film over your work. It’s best to use a soft brush and apply several thin coats. Brush strokes can be an issue with this category of finish. Applying varnish to heavily textured projects can result in pooling and air bubbles. Varnishes do not camouflage surface imperfections such as fingerprints. Rather, they accentuate them. Varnishes are inherently glossy, but can be made to have a satin, semi-gloss, or matte finish by using matting agents. Matting agents are particles that dull the shine of the varnish. Always stir these containers before use, as the matting agent can settle in the bottom, leaving just the glossy varnish at the top of the bottle. I’ll now break down this Varnish category into two types, Acrylic Varnish and Polyurethane Varnish.

Best for: Sealing surface treatments, creating a glossy effect, and enriching translucent projects.

Acrylic Varnishes

In this category, you’ll find artists’ acrylic varnishes, craft store varnishes, and polymer clay brand glazes. Acrylic varnishes contain acrylic polymer emulsion, which is an acrylic resin suspended in water. To save costs, they may also contain vinyl acrylic, vinyl stearate, vinyl acetate, polyurethane, or even polyvinyl acetate (PVA, such as in white glue). The specific formulas are usually a secret, so you’ll never know exactly what is in the varnish you choose.

The only reason this matters is that some of these plastic resins are softened by the plasticizers in polymer clay. (Contrary to myth, plasticizers stay in polymer clay. They do not bake out.) This is why some varnishes, glazes, and sealers work beautifully on wood and paper but become soft or sticky when used on polymer clay. The brand of clay you’re using will make a difference, and some clay-varnish combinations will give you a sticky finish. For this reason, you should always test your particular varnish with the clay you’re using before trusting it to a large or important project. (The same holds true for acrylic paint, by the way.)

Polyurethane Varnish

I’ve separated the polyurethane varnishes because they are marketed differently. But please know that these varnishes still contain acrylic resins. For example, Varathane‘s resin is an acrylic modified urethane. By the same token, many acrylic varnishes contain urethane as part of their resin makeup. So the distinction between these two categories is more one of marketing than chemistry.

Just as with acrylic varnishes, polyurethane is a water-based brush-on varnish and is glossy by nature. Matte versions are created by including matting agents. These varnishes are typically clear to off-white, can leave brush strokes, and dry clear and flexible. Depending on the resins included, some brands of polyurethane can be softened by the plasticizers in your polymer clay. Often, as in the case with Varathane, they won’t cure rock-hard, but it won’t be sticky either. Other varnishes can be sticky, though, so always test a new varnish with the clay you’re using.


Resin creates a nice thick clear coating on polymer clay.

Clear-coat resins are poured onto the surface of your project, and then they harden to form a hard, durable, and thick clear coating. (Read about using resin with polymer clay here.) Resin coatings are quite thick and syrupy and can be frustrating and messy to use. Resin is self-leveling, which means that you need to let it sit for a while so that the surface becomes even. Bubbles can be a problem, but you can usually pop them by waving a heat gun over the top. And just like honey dribbling off your biscuits (scones to you Brits), resin has an annoying way of running off the surface of your project and making a mess. Instead of using a brush, resins are usually poured on, and the sticky liquid is spread on the surface with a toothpick or needle tool. You will use a lot of paper towels with resin projects. Trust me on this. 🙂

Resins are quite hard after curing and are crystal clear. The surface will be extremely glossy and can’t be easily peeled or lifted from a project. While you can apply resin to curved pieces, it is an advanced technique, so I only recommend applying resin to flat pieces until you have a really good feel for how to use it. Resin is lovely on sparkly or mica-covered projects as it will intensify the sparkle. Resin is a rewarding finish, but it has a huge learning curve, and your first few projects will likely incur a few tears and swear words. Always apply resin after baking your polymer clay project. It cannot be baked. There are three types of clear-coat resins as follows.

Best for: Giving flat pieces a thick, glossy finish. Can have a magnifying effect, giving deep dimension to glittery and mica-covered projects.

Epoxy Resin

Common brands of this resin are Envirotex Lite, Amazing Clear Cast (Affiliate Links – learn more here), Little Windows, and ICE Resin (Affiliate Link – learn more here). Epoxy resin consists of two parts, part A and part B, which are mixed in equal portions. Once mixed, a chemical reaction begins, and the resin gradually hardens. It takes about 24-36 hours to fully harden. Epoxy resin will not cure fully if the mixture is incorrect or if the mixture is not fully mixed before pouring. You can apply more coats.

UV Resin

Common brands of this resin are Lisa Pavelka’s Magic Glos (Affiliate Link – learn more here) and UltraDome. These resins are very similar in function and application to epoxy resins, but they cure within 5 minutes when exposed to UV light using a special lamp or a bright sunny day. If you’ve ever had gel nails applied, you’re familiar with the technology here. Interestingly, UV resins are also used as clear coats for automotive use as well. UV Resin is super easy to use as there’s no mixing. Just apply it to your project, wait for it to level, remove bubbles, and cure. But it can still be messy. And the cure will be inhibited, and the surface will remain sticky if you use it over paints or varnishes.

Because UV resins cure before they can run off your piece, they can be used on curved surfaces. Just brush them on. Wait just a minute for the brush strokes to settle, then cure under a light. You can do this with any UV resin, but Teresa Pandora Salgado sells her DeepShine Resin. If you’re new to UV resin, this is a great way to get started.

Polyester Resin

You won’t commonly see polyester resin used in the craft world as it’s pretty noxious. It’s used similarly to an epoxy resin, except that you use a large volume of resin (part A) and a small volume of hardener (part B). I’ve not used this since I was a kid and helped my dad repair a fiberglass tank, so I’m only mentioning it here as an FYI.

Dimensional Glazes

Dimensional glazes are one type of clear-coat finish that can be applied to polymer clay.

Sort of like a cross between a glue and a varnish, dimensional glazes are similar to resin in that they’re syrupy and they can be applied in a thick coating. Common brands are Diamond Glaze, Triple Thick, Mod Podge Dimensional Magic, Aleene’s Jewelry Pendant Gel, and Glossy Accents. You may have seen these liquids used to fill pendant bezels. When poured thick, they will take a few days to fully dry, but they should dry clear and have a sort of a resin effect. Dimensional glazes can be applied with a brush and used as glaze or varnish. All dimensional glazes are glossy – there are no matte versions available.

I am not fond of using this class of products with polymer clay. They are notorious for absorbing humidity and becoming cloudy over time. Some brands get sticky on polymer clay. I’m testing the above four brands, and three of them are already failing. The fourth is holding up well so far, but it’s also the one that my readers tell me is the worst. So I don’t hold much hope for using dimensional glazes with polymer clay.

Best for: Thick, glossy coatings. However, I don’t recommend these due to poor performance on polymer clay.


Waxes can sometimes be used to create a glossy coating on polymer clay.

Renaissance Wax (Affiliate Link – learn more here) has persuasive marketing that’s convinced many people, including many polymer clay artists, that it’s an all-purpose protective material. That’s not exactly true. It is a high-quality microcrystalline wax used to coat metals against corrosion and tarnish. It will also enrich the appearance of materials such as tortoise shell or ivory. Because it’s acid-free, it doesn’t contain chemicals that can degrade artifacts. It is archival. But that doesn’t mean it’s a superior protective coating for all purposes. It can build up and attract dirt.

Renaissance Wax does a lovely job enriching a smooth polymer clay surface. Just apply a thin coating, let dry for a few minutes, then buff with a cloth. This will work sort of like wetting a beach pebble and can enrich a dark clay surface. Wax can also change the appearance of surface treatments, such as paint, chalk, and mica powders. I like to think of waxes as being a surface treatment themselves and not a protectant.

Because waxes apply as a microscopically thin layer to polymer clay, they will do nothing to protect mica powder, glitter, paint, or metal leaf from wear or abrasion and can even remove them. You will not get a glossy shine with a wax. Instead, you’ll get a burnished sheen, but only when used on an already smooth surface. Wax applied to a textured surface will be white and unattractive.

There are other waxes that work just as well. Neutral shoe polish and paste wax (Affiliate Link – learn more here) both work nicely on polymer clay to create a warm, enhancing sheen. But frankly, so does Vaseline, at a tiny fraction of the cost.

Best for: Deepening and enriching dark colors, giving a warm sheen to smooth clay.

Liquid Polymer Clay

Liquid polymer clay can be used instead of polymer clay glazes, sealers, and varnishes.

Liquid clays are essentially polymer clay without the binders that turn it into a putty. They have many uses, such as acting as a glue, a transfer medium, and a clay thinner. You can also use liquid polymer clays as a glaze or sealer. Liquid clays have the advantage of always being 100% compatible with polymer clay and will not result in stickiness. There are three main well-known brands of liquid polymer clay. You can read more about these liquid clays in my article on using them as a clearcoat here.

Best for: Encasing inclusions, sealing surface treatments. Always clay-safe.

Kato Liquid Polyclay

Also known as Kato Liquid or Kato Sauce, this liquid has the consistency and appearance of thinned white glue. To use as a varnish, apply a very thin coat with your finger or a brush. Allow to level, then bake. After baking, you will need to use a heat gun to make the thin layer of clay crystal clear and shiny.

Fimo Liquid

Fimo Liquid used to be called Fimo Deco Gel. It is a syrupy, runny, cloudy liquid. Apply to your clay, allow to settle, and then bake. It will become clear during baking. Of the three main brands of liquid polymer clay, Fimo Liquid is the only one that will remain fairly clear when cured in a thick layer. To use as a varnish, apply to the clay in a thin coating. Allow to settle and level, then bake. A heat gun will make it more shiny, but it won’t be as shiny as Kato Liquid.

Translucent Liquid Sculpey

This stand-by, also called TLS, is similar to the other liquid clays and can also be used as a glue and thinner. But it does not bake particularly clear. Thick layers will be opaque. It can be effectively used as a varnish, however, by using a cosmetic sponge to dab the TLS onto your clay surface. Wait a few minutes for it to settle and level (a bit) and then bake. Afterward, thin layers will be invisible, but the surface will be matte. If you use a heat gun on cured TLS, it will become glossier, giving a satin finish.

Liquid Sculpey Clear

Brand new on the market, Clear Liquid Sculpey is similar to Kato Liquid Polyclay in that it can give a perfectly clear coating when it’s clarified with a heat gun. Baking it in the oven at normal clay-curing temperatures will result in a cloudy finish. It really does need the high heat of a heat gun. It will be just slightly less shiny than Liquid Kato.

Spray Varnish

Spray varnish can be used as a polymer clay glaze, sealer, and varnish.

Spray varnish seems like such a perfect solution. Just take your project out on the porch, spray it real quick, come back in, and you’re done. But sadly, very few brands of spray varnish will work with polymer clay. MOST of them will be softened by the plasticizer in polymer clay and stay sticky. PYM II (now discontinued and nearly impossible to find) is a unique spray acrylic coating that does not stay sticky and works well with polymer clay. PYM is not glossy or matte. Rather, it’s sort of a semi-gloss finish. Multiple coats will give a more durable finish but do let it dry between coats. Many thin coats are far better than one thick one. Read about my experiments with spray sealers hereHelmar Crystal Kote Matte is another spray varnish that works well with polymer clay. It is nearly invisible on your project.

You will want to use a spray varnish when you need to quickly seal and stabilize surface treatments such as mica powders, chalks, and glitter. Sprays also work nicely to apply a varnish coating onto textured surfaces.

Best for: Sealing surface treatments, especially mica powders. Great on textured items where varnish would pool.

Embossing Powder

Clear embossing powder is one type of clear-coat finish that can be applied to polymer clay.

Embossing powder is a wax-like powder that is traditionally applied to a design on paper, then melted with a heat gun to create a raised, “embossed” design. Clear embossing powder is popularly used in crafts because it can be melted in a special melting pot and then used as a clear coating material. A common variant of this embossing powder is called Ultra Thick Embossing Enamel (UTEE). UTEE can be used to coat polymer clay projects, giving a thick, clear surface like resin. I don’t recommend UTEE for glazing and varnishing purposes with polymer clay because it isn’t very durable. It’s not very flexible and will readily flake off baked polymer clay. It can turn cloudy over time. It is also easily scratched.

Best for: Not recommended as a polymer clay glaze, sealer, or varnish.


Glues can sometimes be used to create a clear-coat finish that can be applied to polymer clay.

I’m adding this as a catch-all category because there are some glues that can be used as a polymer clay glaze, sealer, or varnish.

Mod Podge

Mod Podge is a decoupage medium that paper crafters use as a “sealer”. Therefore new polymer clayers sometimes advocate their use as a glaze, sealer, and varnish as well. Mod Podge is a variety of thinned white PVA glue, similar to Elmer’s glue. It is available in glossy, satin, and matte versions. It is white and dries clear. But Mod Podge does not make a good polymer clay glaze or varnish. It is very difficult to apply without obvious brush strokes. After drying, if it dries at all, it can stay sticky in high-humidity applications. Water left on the surface will turn white, and the Mod Podge will soften. I strongly recommend this not be used as a polymer clay glaze, sealer, or varnish.


Woodworkers know that cyanoacrylate (CA) can make a fantastic coating for wood. But it works very well with polymer clay as well. Cyanoacrylate is also known as super glue. And yes, some varieties of CA are specifically used to create a tough, durable, and clear surface coating. Because a lathe is typically used, it’s beyond the scope for most routine polymer creations. But it’s something I want to explore further at some point. A CA finish is what Ed Street uses to put a super-smooth finish on Toni Ransfield’s pens. You can read more about the process here on Toni’s site.

Liquid Fusion

Liquid Fusion is a urethane glue that is slightly amber-colored and crystal clear. It can be poured on the surface of flat polymer clay and left to dry. It will take several days, but you’ll be left with a smooth, glossy, hard finish similar to resin.

Sanding and Buffing

The Sanding and Buffing Polymer Clay eBook includes a bonus tutorial showing how I created this beautiful mica shift piece.

When done well, a sanded and buffed smooth polymer clay surface is considered by many to be the best finish. Sanding and buffing is hard to beat because there will never be any brush strokes, stickiness, cloudiness, or other chemical incompatibilities. Smoothly sanded polymer clay is a tactile pleasure that you can’t help but rub between your fingers because it just feels so nice. Unbuffed, a sanded finish will be completely matte. Buff it a bit for a warm satin sheen. If you properly buff smooth polymer clay with a high-speed buffer, you can get a finish that is just as smooth and glossy as resin or glass. In fact, it’s quite difficult to get this kind of flawless glossy surface with varnishes or glazes. Sanding and buffing has a reputation for being difficult and can lead to painful fingertips, but it doesn’t have to be that way.

If you want to know how to get an absolutely perfect shine on polymer clay with sanding and buffing, with minimal effort, I recommend that you check out my Sanding and Buffing eBook. It is a comprehensive 120-page guide that explains everything I know about sanding and buffing. I discuss the types of sandpaper, kinds of buffers, using tumbling machines, Dremel, varnishes, and even whether you even need to sand at all. Here’s where you learn more about the Sanding and Buffing eBook. If you want a shiny, smooth polymer clay surface, this eBook will get you there.

Sand better, not harder

Everyone loves a perfectly smooth, glassy finish, but it seems to be elusive. Does your polymer clay look scratched and rough after sanding? This course will change everything.

129 thoughts on “Understanding Polymer Clay Glaze, Sealer, and Varnish”

  1. I’ve made some earrings from polymer clay, and used acrylic paint and a design from a silk screen on top. I have used Sculpey satin glaze as I want to protect the paint from chipping and I like the satin sheen it gives. I’ve noticed that I need to re sand some of the design to clean it up abit, can you sand over the glaze? And then re glaze it again? Thanks

  2. polymer clay beginner

    Dear Ginger,

    I would like my finished items to look natural (as they are) but still use glaze to protect them from dust. Should I use satin or matte finish? Thank you!

  3. Hello,
    I already used fimo gloss varnish on some polymer clay jewelry but I would like to use sculpey bake and bond instead of superglue to attach the posts. Is it okay to bake after the varnish was already applied? Thank you!!!

  4. Thank you for all you do! I used polyurethane on white clay, and thought it would be a good idea to cure the piece for another 10 minutes or so. I regret doing so as the clay now looks yellow. Can I sand off the polyurethane or will that make matters worse?
    Thank you, Ginger!

    1. If it was water-based polyurethane, baking again shouldn’t change the color. Regardless, if you’d like to remove the varnish, you can use isopropyl alcohol to dissolve it. On the other hand, if you use oil-based polyurethane, it is naturally slightly yellow (because it’s made with linseed oil) and that’s likely the cause of the yellowing rather than the baking.

  5. Excellent information and special praise to the editor.

    I’m hoping to create small custom shapes (sea grasses, starfish, turtle) as accents in an upcoming bathroom shower project. The shapes would be set among cutouts in the wall tiles, thin set underneath and grouted in place. I’m an experienced home improvement person along with being an artist so this seemed like a good way to make boring subway tile turn out as a custom project. I have a wall mural with a blue heron as a centerpiece for the main shower wall and want to play off that with more texture and dimension – and polymer clay shapes came to mind. Dipping them in resin was going to be my waterproofing solution, with the understanding that i would need to pay close attention to assure complete coverage since resin does run.

    Do you have a different suggestion? Or is my idea totally crazy?

    Thank you so much for the work you do and sharing your expertise!

  6. As always, terrific and informative article Ginger! To other readers – you’ve got to buy an ebook or 2, 3, 4…she truly is the best at explaining and instructing In an easy, fun way. I’ve been working with polymer clay for decades, and I still refer to her free articles and ebooks all the time. I’ve saved tons of money, and I only wish I found this site sooner. All the products I’ve tried that failed over the years… Ugh haha.
    So. Since you’ve read this particular article –

    BUY HER EBOOK on SANDING AND BUFFING! There’s no comparison to a really well sanded and buffed clay piece. And to do it well you need the ebook.

  7. If you are using a sealant to protect a painted surface, is it important to match the brand of sealant to the clay? Can you use Fimo on Sculpey and vice versa, for example?

  8. Hi, I would like to make a clay product that can withstand dropping over and over again. I would like to know if there is anything that comes to mind that can keep it from breaking eventually?

    Thank you.

    1. I’ve had polymer clay keychains that held up wonderfully over time. Properly baked polymer clay is quite durable. It can’t handle flexing repeatedly, but it should handle being dropped quite well. Just make it thick enough and bake it properly.

      1. How thick is thick enough? & How to bake properly? Or a link where you explain those two things? Thanks Bunches!

  9. This is THE BEST and most comprehensive polymer info thing I’ve ever come across. I love how thorough you are. Thank you! Getting the ebook now. Really appreciate it.

  10. I am trying to make a snow globe for my niece. It is highly intricate, and made of super sculpey and I intend to paint it with acrylics, but I can’t for the life of me figure what sealant to use.
    I know epoxy resin would likely work, but I’ve the work’s intricate nature, that frightens the crap out of me. Do you know anything about best sealants for acrylic paints and snow globes?

  11. I recently did a project with cheap modelling clay that dries on its own. I’d like to put a clear coat on it to make it look more glossy and finished. What would you recommend?

      1. Hi! I have an Etsy shop that only uses environmentally-friendly materials and products which is why I’d like to use cold porcelain air dry clay as opposed to polymer clay for making little earrings, But i need them to be waterproof. Any suggestions for a great eco-friendly waterproof sealant for this kind of project?

        1. Use whatever you feel comfortable using. Be aware, however, that nearly all sealers are/contain plastic, as does most cold porcelain. You could use linseed oil, perhaps, but then you’d need to look into the cultivation practices and sourcing of the oil.

  12. Thank you so much, this little post answered EVERYTHING I needed to find out in one place, what a great help, I have subbed thanks again

  13. Shannon M Smith

    Hi I just recently did a project with Polymer clay. I used Pearl ex metalic finish dust to make it look metalic however there were some area’s where I had to re-dust later after the bakeing and I want to seal that into the piece. They will be used on a bathroom sink so they could often get occasionally splashed with water. How can I seal this. I am understanding in your article its not typically required to seal it after baking and curing. However, this powders where applied after the fact (quiet a bit before in the molds)?? after reading your articles I’m not sure what to use. I want it to have a shiney finish. maybe I should have used another medium, I D K?

    1. Polymer clay itself does not need to be sealed the way that wood or paper does. It’s plastic. But the surface treatments you apply to polymer clay DO need to be sealed if the item will be subjected to wear. I would use a clay-compatible varnish for this. Take your pick from the ones listed in the article here: Testing 41 Polymer Clay Sealers.

      1. Shannon M Smith

        Woah, I cant thank you enough for responding and your follow up advice was very helpful thank you so much!!! i expected a POSSIBLE reply in a few days to week but I was shocked to have gotten such a fast response your freeakin aaaaahmmmaaaazun!

  14. I am planning to make a snow globe using polymer clay for the figures, but am more comfortable with acrylic painting rather than trying to use various coloured clays. I have found that polymer clay should work fine, but I haven’t been able to find any advice as to whether painted clay should be sealed, or whether the acrylic paint would be secure.
    Do you have any advice?

  15. Hi can I ask, I am making bauble with Sculpey III just to use it up, I would like toco er it with glitter and I thought of using mod Podgorica and then pour glitter over. But reading post on glues it might not be a good idea, can you recommend something else

  16. Hi Ginger have you by any chance tested Pledge ‘revive it’ floor gloss. I have just started using this and love the shine.

  17. Thanks for such a thorough and informative article! I’ve been making with polymer clay for several years and currently use a water-based sealer when I need to seal my pieces, but I want to start making some critters to decorate my houseplants, so I need something that won’t dissolve if/when it gets wet. Based on the info above, I’m thinking a brush-on uv resin might be my best bet, but I didn’t see anything specifically related to waterproofing, unless I missed it?

    1. None of the coatings recommended above will dissolve in water (aside from dimensional glazes). But water can get under them and lift them. In fact, resin is terrible for this. Polymer clay is vinyl plastic and therefore does not need to be sealed. It is naturally waterproof. Don’t use any sealer. Just use polymer clay itself. You can read more about sealing here: https://thebluebottletree.com/seal-polymer-clay/

  18. I make baked polymer clay babies for a prolife group. Then I use acrylic paint for hair and eyes. Cheecks and creases are done using chalks. Do you think I need to seal them with any type of product?

    1. It’s really hard to say. The only reason you’d need to seal them is if they’re rubbing or wearing off easily. Polymer clay itself does not need to be sealed. So it’ll be up to you as to whether or not you feel your project would benefit by adding a clearcoat over the top of them.

    2. Hello I’m looking to coat sparkly glittery jewellery that will be touched . I’ve looked at varathane it’s very expensive! Any other i can use that’s not sticky please.

  19. The info here is wonderful. I am new to PC and I making checkers and backgammon stones. What would be the best sealer for them since they will be handled a lot? I have made them with white clay, with a moderately deep imprint and will be adding color with acrylic paint.

  20. Hi. 2 years ago I made the mistake of spraying polymer ornaments with acrylic sealing spray. They’re ornaments made of my then baby daughters foot prints. They’re still sticky. I’ve kept them though I don’t hang them on the tree every year because of this. Can this issue be remedied? 🙁

    1. I have heard that there are some food-safe resins. But that is just the material itself, not the application or use on a polymer bowl. It’s important to realize that being “food safe” is an official designation that’s awarded to items after they’ve demonstrated their ability to be safe for food use. Because no testing organization can evaluate how you make a polymer clay bowl, nothing that we make with our hands can be labeled as “food safe”. So no, a polymer bowl won’t be “food safe” by adding resin. But that’s a legal designation, not a practical one. Can you, personally, for personal use, use a food-safe resin on your polymer bowl? It’s up to you. Can you sell them as housewares designed for use with food? Nope. Does that help?

  21. Love all the information! Could you recommend me a product? I’m currently sculpting decent size sculptures and then painting acrylic afterwards. What would be the best product to get to protect the paint from wear?

    1. Why does a sculpture need to be protected from wear? It’s not jewelry, surely? It’s a common misnomer that painted polymer clay needs to be sealed. It doesn’t, unless it will be handled extensively and in that case I’d recommend a varnish called Varathane. You can read about it here: Varathane.

  22. I have a sealant/troubleshooting question. I sealed a few pieces with Minwax poly before realizing that it’s oil-based, not water-based–so now I’m worried about it getting sticky over time. Can I add a thin coat of liquid polymer over the pieces to re-seal them, over the dried oil-based sealant, to prevent stickiness?

    1. Oil-based varnish can work well with polymer clay. The drawback is that it’s linseed oil based and will therefore be yellow. If it has dried and is not sticky now, then it will likely be just fine. No need to re-seal.

  23. Ginger, So happy that I found your site, such wonderful information! I am in a pickle trying to repair something for a friend that was custom made. Artist is in another country and there is no time to send it back for repair. It is a Poly clay baked wedding cake topper and the bottom that supports the figures broke in transit. The artist recommended fixing it with a little Mod Podge. I do not believe that will hold. It appears that it was sealed with Mod Podge and I do not want the glue to be incompatible. I am thinking of using an epoxy and also adding some type of support material to the bottom for stability since it is so thin and could break again.
    What would you recommend for a support material that can be glued on the bottom and go on a cake and is epoxy the best choice for gluing the pieces back together as I cannot drill any where to put in a support pin. Thank you,

    1. Your suspicions are correct and Mod Podge will not likely be a suitable repair. Without seeing the piece, I can’t guarantee that any repair will hold because the piece just might be structurally unsound rather than merely a breakage issue. Generally, we use a gel superglue rather than epoxy. I would use Loctite Gel Control to glue the pieces back together. It won’t be a “proper” repair, but it will likely be good enough to last through the wedding.

  24. Fantastic information. I can’t thank you enough.
    Hi. I make necklace pendants, hair pieces, drinking vessel embellishments, pins and so forth. In other words, items that encounter heavy, every day wear and tear. I’m flustered over finishes at the moment. I would like your opinion on which new ones would be best for me to purchase and try. I very much strive to create an end result that resembles it’s poly clay self as little as is possible. I use Kato brand clay, as i find it to be slightly more brittle than Cernit, but still very strong and has the slightly harder finish ideal for jewelry like items. The more like metal and wood it looks, the better. I use a lot of sparkly powder pigments to achieve my desired color, along with rub-n-buff and metal leaf. And i incorporate metal bits, genuine stones and cz rinestones. But I find that my coating on relief points tends to wear off in short time, dulling and completely removing the metallic color underneath. I use a polyurethane spray varnish right now. I imagine I could do with a few extra coats. But in the end, what I really want is a product I don’t have to touch up after a few weeks and that I can proudly ensure to my customers will last for a decent time, while of course still not requiring such a heavy coating that it fills in and blurs the finer details. They are heavy with tiny details. As far as durability goes, I have everything else down pat. So if such a top coat exists, I’m hoping you can tell me which one is for me.

    1. Anytime you use any surface treatment, it will have limited durability. Period. It’s just so thin. All varnishes are merely a thin layer of plastic. So even the best ones are just a thin layer protecting a thin surface treatment. No wonder they wear through! In addition, most varnishes are not as hard on polymer clay as they would be on wood due to chemical interactions. When something is subject to a lot of wear, having anything on the surface will eventually wear through.

      That being said, you might want to explore using resin. It’s thicker and harder and would likely have more durability. Of course, it might not give you the look you’re after.

Comments are closed.

Scroll to Top

There’s a lot of bad info out there. THIS info is different. Sign up now to get this game-changing  polymer clay info from Ginger.

You’ll also be on the list to get Ginger’s monthly newsletters on polymer clay.

Almost There


Check your email/spam


Click to confirm


Watch for welcome

Check your spam folder. Email programs are very aggressive and you’ll likely find lots of missing emails in there!